Similar Henkel Loctite 510 Quality Gasketing & Sealing

                             Similar Henkel Loctite 510 Quality Gasketing & Sealing

                                  From Shirley(hengying@cnhybond.com  0086-18927302778, Skype:hengying11)

1.Product Description

Technology: Acrylic

Chemical type: dimethacrylate ester

Appearance(uncured): Opaque pink paste

Components: One component-require

Viscosity: High

Cure Anaerobic

Application Gasketing and sealing

Strength Medium

CNHYBOND 510 cures when confined in the absence of air between close fittingmetal surfaces, this product is a general gasketing product suitable for habd

dispensing or screen printing.

2.Typical Properties of Uncured Material 

Specifci gravity@25℃ 1.1

Viscosity ,Brookfield,HBT 25℃,mpa.s(cp):

Spindle TC,speed2.5rpm,helipath: 200,000 to 750,000

3.Instant Sealing Capability

Anaerobic sealants have the ability to resist low on-line test pressures while uncured,this test was performed with uncured product immediately after assembly of an annular polycarbonate sealing surface with an internal diameter of 50 mm and external diameter of 70mm 

Pressure Resistance ,Mpa:

Induced Gap 0mm 0.02

Induced Gap 0.125mm 0.01

INDUCED Gap 0.25mm 0.01

4.Typical Performance of Cured Material 

Adhesive properties

Cured for 1 hour@22℃

Compressive sherar strength iso 10123

Steel pins and collars(grit N/MM2 >1

Cured for 24 hours@22℃

Compressive shear strength ,iso 10123

Steel pins and collars(grit ,N/MM2 >7.5)

Lap shear strength ,iso4587

Steel(grit blasted) N/MM2 5

Tensile strength , iso 6922

Steel(grit blasted) N/MM2 7.5

5.Directions for Use

A. For best performance bond surfaces should be clean and free from grease

B. The product is designed for close fitting flanged parts with gaps up to 0.25mm

C. Apply manually as a continuous bead or by screen printing to on surface of the flanges

D. Low pressures(<0.05mpa) may be used when testing to confirm a complete seal immediately after assembly and before curing

E. Flanges should be tightened as soon as possible after assembly to avoid shimming

6.Storage

Store in the unopened container in a dry area, and storage instruction are indicated on the label of the

bottle.

Optimal Storage: 2 °C to 8 °C. Storage below 2 °C or greater than 8 °C can adversely affect

product properties. Material removed from containers may be contaminated during using. Do not return

product to the original container. Heng ying Corporation cannot assume responsibility for product which

has been contaminated or stored under conditions other than those previously indicated.

7. Note

The data contained herein are furnished for information only and are believed to be reliable. We cannot

assume responsibility for the results obtained by others over whose methods we have no control. It is the

user's responsibility to determine suitability for the user's purpose of any production methods mentioned

herein and to adopt such precautions as may be advisable for the protection of property and of persons

From any hazards that may be involved in the handling and then use. In light of the foregoing, HENY

YING Corporation specifically disclaims all warranties expressed or implied, including warranties

of merchantability or fitness for a particular purpose, arising from sale or use of HENG YING

Corporation’s products. HENG YING Corporation specifically disclaims any liability for

consequential or incidental damages of any kind, including lost profits. The discussion about

various processes or compositions is not to be interpreted as representation that they are free from

domination of patents owned by others or as a license under any HENG YING Corporation patents that

may cover such processes or compositions. We recommend that each prospective user test his

proposed application before repetitive use, using this data as a guide.