Loctite 648 Equivalent Green High Strength Retaining Compound
from Shirley(hengying@cnhybond.com 0086-18927302778 Skype:hengying11)
1.Product Description
HYBOND 648 provides the following product characteristics:
Technology: Acrylic
Chemical Type: Urethane methacrylate
Appearance (uncured): Green liquidLMS
MComponents: One component - requires no mixing
Viscosity: Low
Cure : Anaerobic
Secondary Cure: Activator
Application :Retaining
Strength: high
HYBOND 648™ is designed for the bonding of cylindrical fitting parts. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. Typical applications include holding gears and sprockets onto gearbox shafts and rotors on electric motor shafts
2.Typical Properties of uncured material
Specific Gravity @ 25 °C 1.13
Flash Point - See MSDS:
Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP):
Spindle 2, speed 20 rpm 400 to 600LMS
Viscosity, EN 12092 - MV, 25 °C, after 180 s, mPa·s (cP):
Shear rate 129 s-1 300 to 600
3.Typical Properties of cured material
Physical Properties
Coefficient of Thermal Expansion, ASTM D 696, K-1 80×10-6
Coefficient of Thermal Conductivity, ASTM C177,
W/(m·K)
0.1
Specific Heat, kJ/(kg·K) 0.3
4.Typical Performance of cured material
Adhesive Properties
Cured for 15 minutes @ 22 °C
Compressive Shear Strength, ISO 10123:
Steel pins and collars N/mm² ≥13.5LMS
(psi) (≥1,957)
Cured for 24 hours @ 22 °C
Compressive Shear Strength, ISO 10123:
Steel pins and collars N/mm² ≥25LMS
(psi) (≥3,625)
5.For Assembly
(1). For best results, clean all surfaces (external and internal) with a HYBOND cleaning solvent and allow to dry.
(2). If the material is an inactive metal or the cure speed is too slow, spray with Activator 7649™ and allow to dry
(3). For Slip Fitted Assemblies, apply adhesive around the leading edge of the pin and the inside of the collar and use a rotating motion during assembly to ensure good coverage.
(4). For Press Fitted Assemblies, apply adhesive thoroughly to both bond surfaces and assemble at high press on rates.
(5). For Shrink Fitted Assemblies the adhesive should be coated onto the pin, the collar should then be heated to create sufficient clearance for free assembly.
(6). Parts should not be disturbed until sufficient handling strength is achieved
6.For Disassembly
Apply localized heat to the assembly to approximately
250 °C. Disassemble while hot.
7.For Clean up
Cured product can be removed with a combination of soaking in a HENG YING solvent and mechanical abrasion such as a wire brush.
8.Storage
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container.HYBOND Corporation cannot assume responsibility for product which
has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.
We have new company pages on facebook, google, linkedin, and please follow us, thank you.
https://plus.google.com/u/0/b/117466620353553764866/117466620353553764866/admin/?tab=XX#117466620353553764866/posts?tab=XX
Can i use a solvent instead of heat. I dont want to damage my electrical motor. Maybe offer a substitute retaining compound that uses lower heat to remove. My gear has a keyway that hold a gear on the motor shaft. The motor shaft is stainless. Gear is aluminium. 450°F i feel is too much for the motor shaft going straight into the motor.
ReplyDelete