Loctite 620 Equivalent Anaerobic Threadlocker Adhesive

               Loctite 620 Equivalent Anaerobic Threadlocker Adhesive

                                                               from Shirley(hengying@cnhybond.com   0086-18927302778  Skype:hengying11)

1:PRODUCT DESCRIPTION

HYBOND 620 provides the following product characteristics:

Technology: Acrylic

Chemical Type: methacrylate ester

Appearance (uncured): Green  liquidLMS

MComponents:  One component - requires no mixing

Viscosity: high

Cure : Anaerobic

Secondary Cure: Activator

Application :Retaining

Strength: Medium to high

HYBOND 620 is designed for the bonding of cylindrical fitting parts. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. Typical applications include locating pins in radiator assemblies, sleeves into pump housings and bearings in auto transmissions. Particularlysuitable for applications where temperature resistance up to 200°C is required.

2: TYPICAL PROPERTIES OF UNCURED MATERIAL

M LM Specific Gravity @ 25 °C 1.16

Flash Point - See MSDS

Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP):

Spindle 5, speed 20 rpm 5,000 to 12,000LMS

Viscosity, EN 12092 - MV, 25 °C, after 180 s, mPa·s (cP):

Shear rate 129 s-1 1,200 to 2,400S

3:TYPICAL PROPERTIES OF CURED MATERIAL

Physical Properties:

Coefficient of Thermal Expansion, ASTM D 696, K-1 80×10-6

Coefficient of Thermal Conductivity, ASTM C 177,

W/(m·K)

0.10

Specific Heat, kJ/(kg·K) 0.30

Elongation, at break, ASTM D 412, % <1

4:TYPICAL PERFORMANCE OF CURED MATERIAL

Adhesive Properties

After 24 hours @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥17.20LMS

(psi) (2,495)

Cured for 24 hours @ 22 °C, followed by 24 hours @ 177 °C,

tested @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥24.10LMS

(psi) (3,495)

5:For Assembly

(1). For best results, clean all surfaces (external and internal) with a HYBOND cleaning solvent and allow to dry.

(2). If the material is an inactive metal or the cure speed is too slow, spray with Activator  7649™ and allow to dry.

(3). For Slip Fitted Assemblies, apply adhesive around the leading edge of the pin and the inside of the collar and use a rotating motion during assembly to ensure good coverage.

(4). For Press Fitted Assemblies, apply adhesive thoroughly to both bond surfaces and assemble at high press onrates.

(5). For Shrink Fitted Assemblies the adhesive should be coated onto the pin, the collar should then be heated to create sufficient clearance for free assembly.

6:For Disassembly

Apply localized heat to the assembly to approximately

250 °C. Disassemble while hot.

7:For Clean up

Cured product can be removed with a combination of soaking in a HENG YING solvent and mechanical abrasion such as a wire brush.

8:Storage

Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.

Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container.HYBOND Corporation cannot assume responsibility for product which

has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.