Loctite 272 Equivalent High Temperature High Strength Threadlocker

     Loctite 272 Equivalent High Temperature High Strength Threadlocker

                                                                  from Shirley(hengying@cnhybond.com   0086-18927302778  Skype:hengying11)

1. Red color, anaerobic type, anaerobic glue

2. High intensity, high viscosity, high-temperature resisting

3. Use for locking and sealing bolts under high temperature.

4. Applicable to lock the bolt stud of cylinder end.

5. Product introduction:

272 is a kind of one-component, high viscosity, high intensity, anaerobic type screw thread lock sealant. This product is applied to two close-fit metal surfaces and solidifies when isolating with air.

6. Product application:
Avoid looseness and leakage of the screw thread fastener. Use for permanently locking the bolt stud of cylinder end. Especially applicable to the locking and sealing bolts under high temperature

7. Product character

Typical value	scope
Basic chemical component	methyl acrylic acid ester
color	Red
viscosity @25°C, mPa.s	9500
proportion	1.12
flash point (℃)	>93
maximum gap filling（mm）	0.25
fixed time（min）	15                    10-20
solidification time under room temperature（min）	60
performance after solidification
complete solidification time under room temperature （hrs）	24
destabilizing moment（N· m）	23
average dismantling moment（N· m）	24
operating temperature（℃）	54～230

Aging under the following conditions and tested at temperature of 22

solvent	temperature  (℃ )	after 30 days initial intensity remaining rate (%)
engine oil	87	62
gasoline	87	62

8. Instructions

(1).The applied side should be washed clean, dry and oil-free, which choose 755 abluent to have the best effect.

(2).Apply enough glue on the bolt to fill up the whole thread engagement; this product will have optimum result on the thin sub of below 0.05mm.

(3).As to the king size screw thread, the large clearance will affect the speed of solidification and intensity. This product can alleviate the friction caused by assemblage (torsional moment and tension ratio), which should be fixed in advance when tight up the screw thread to the critical value. 

9. Safety notice

This product contains crylic acid and methyl acrylic acid hydroxide propyl propionate, which is irritative to skin and eyes. If the liquid gets to the skin should rinse with water at once; if eyes, should rinse with water and consult the doctor. 

10. Packaging   50ml. 250ml

11. Storage condition
Shelf life (in sealed container) can be up to 18 months in a cool and dry place with temperature ranging from 15 to 28.

Loctite 510 Equivalent Gasket Eliminator High Temperature Flange Sealant

           Loctite 510 Equivalent Gasket Eliminator High Temperature Flange Sealant

                                                                           from Shirley(hengying@cnhybond.com   0086-18927302778  Skype:hengying11)

1.Product Description

Technology: Acrylic

Chemical type: dimethacrylate ester

Appearance(uncured): Opaque pink paste

Components: One component-require

Viscosity: High

Cure Anaerobic

Application Gasketing and sealing

Strength Medium

CNHYBOND 510 cures when confined in the absence of air between close fitting metal surfaces, this product is a general gasketing product suitable for hard dispensing or screen printing.

2.Typical Properties of Uncured Material 

Specifci gravity@25℃ 1.1

Viscosity ,Brookfield,HBT 25℃,mpa.s(cp):

Spindle TC,speed2.5rpm,helipath: 200,000 to 750,000

3.Instant Sealing Capability

Anaerobic sealants have the ability to resist low on-line test pressures while uncured,this test was performed with uncured product immediately after assembly of an annular polycarbonate sealing surface with an internal diameter of 50 mm and external diameter of 70mm 

Pressure Resistance ,Mpa:

Induced Gap 0mm 0.02

Induced Gap 0.125mm 0.01

INDUCED Gap 0.25mm 0.01

4.Typical Performance of Cured Material 

Adhesive properties

Cured for 1 hour@22℃

Compressive sherar strength iso 10123

Steel pins and collars(grit N/MM2 >1

Cured for 24 hours@22℃

Compressive shear strength ,iso 10123

Steel pins and collars(grit ,N/MM2 >7.5)

Lap shear strength ,iso4587

Steel(grit blasted) N/MM2 5

Tensile strength , iso 6922

Steel(grit blasted) N/MM2 7.5

5.Directions for Use

A. For best performance bond surfaces should be clean and free from grease

B. The product is designed for close fitting flanged parts with gaps up to 0.25mm

C. Apply manually as a continuous bead or by screen printing to on surface of the flanges

D. Low pressures(<0.05mpa) may be used when testing to confirm a complete seal immediately after assembly and before curing

E. Flanges should be tightened as soon as possible after assembly to avoid shimming

6.Storage

Store in the unopened container in a dry area, and storage instruction are indicated on the label of the

bottle.

Optimal Storage: 2 °C to 8 °C. Storage below 2 °C or greater than 8 °C can adversely affect

product properties. Material removed from containers may be contaminated during using. Do not return

product to the original container. Heng ying Corporation cannot assume responsibility for product which

has been contaminated or stored under conditions other than those previously indicated.

Loctite 603 Equivalent Retainer 603 anaerobic sealant

                  Loctite 603 Equivalent Retainer 603 anaerobic sealant

                                                                                   from Shirley(hengying@cnhybond.com  0086-18927302778  Skype:hengying11)    

1:PRODUCT DESCRIPTION

HYBOND 603 provides the following product characteristics:

Technology: Acrylic

Chemical Type: Urethane methacrylate

Appearance (uncured): Green  liquidLM

MSComponents: One component - requires no mixing

Viscosity: low

Cure : Anaerobic

Secondary Cure: Activator

Application :Threadlocking

Strength: High

HYBOND 603 is designed for the bonding of cylindrical fitting parts, particularly where consistently surfaces cannot be assured. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. Typical applications include retaining roller bearings or oil impregnated bushings into housings.

2: TYPICAL PROPERTIES OF UNCURED MATERIAL

MSSpecific Gravity @ 25 °C 1.1

Flash Point - See MSDS

Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP):

Spindle 1, speed 20 rpm 100 to 150LMS

Viscosity, EN 12092 - MV, 25 °C, after 180 s, mPa·s (cP):

Shear rate 277 s-1 90 to 180

3:TYPICAL PERFORMANCE OF CURED MATERIAL

Adhesive Properties

After 24 hours @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥22.5LMS

(psi) (3,260)

After 30 minutes @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥13.5LMS

(psi) (1,960)

4:For Assembly

1. For best results, clean all surfaces (external and internal) with a HYBOND  cleaning solvent and allow to dry.

2. If the material is an inactive metal or the cure speed is too slow, spray with Activator  7649™ and allow to dry.

3. For Slip Fitted Assemblies, apply adhesive around the leading edge of the pin and the inside of the collar and use a rotating motion during assembly to ensure good coverage.

4. For Press Fitted Assemblies, apply adhesive thoroughly to both bond surfaces and assemble at high press on rates.

5. For Shrink Fitted Assemblies the adhesive should be coated onto the pin, the collar should then be heated to create sufficient clearance for free assembly.

6. Parts should not be disturbed until sufficient handling

strength is achieved.

For Porosity Sealing

1. Clean area and apply localized heat to the area to

approximately 121°C.

2. Allow to cool to approximately 85°C and apply the

product.

5:For Disassembly

Apply localized heat to the assembly to approximately

250 °C. Disassemble while hot.

6:For Clean up

Cured product can be removed with a combination of soaking in a HENG YING solvent and mechanical abrasion such as a wire brush.

7:Storage

Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.

Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container.HYBOND Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

Loctite 609 Quality Bearing Mount Green Retaining Compound

                Loctite 609 Quality Bearing Mount Green Retaining Compound

                                   from Shirley(hengying@cnhybond.com  0086-18927302778  Skype:hengying11)

1:Product Description

HYBOND 609 provides the following product characteristics:

Technology: Acrylic

Chemical Type: methacrylate ester

Appearance (uncured): Green liquid

Components: One component - requires no mixing

Viscosity: low

Cure : Anaerobic

Secondary Cure: Activator

Application :Retaining

Strength: Medium

HYBOND609 is designed for the bonding of cylindrical fitting parts. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. Typical applications include rotor to shafts in fractional and subfractional horsepower motors. Locks bushings and sleeves in housings on shafts. Augments press fits.

Mil-R-46082B   HYBOND 609 is tested to the lot requirements of Military   Specification Mil-R-46082B.

2: Typical Properties of Uncured Material 

Specific Gravity @ 25 °C 1.10

Flash Point - See MSDS

Viscosity, Cannon Fenske #300, ISO 3104, mPa·s (cP) 110 to 140LMS

3:Typical Properties of Cured Material 

Physical Properties:

Coefficient of Thermal Expansion, ASTM D 696, K-1 80×10-6

Coefficient of Thermal Conductivity, ASTM C 177,W/(m·K) 0.10

Specific Heat, kJ/(kg·K) 0.30

Elongation, at break, ASTM D 412, % <2

4:Typical Performance of Cured Material  

Adhesive Properties

After 24 hours @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥15.80LMS (psi) (≥2,290)

After 1 hour @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥10.30LMS   (psi) (≥1,490)5

5:For Assembly

(1). For best results, clean all surfaces (external and internal) with a HYBOND  cleaning solvent and allow to dry.

(2). If the material is an inactive metal or the cure speed is too slow, spray with Activator  7649™ and allow to dry.

(3). For Slip Fitted Assemblies, apply adhesive around the leading edge of the pin and the inside of the collar and use a rotating motion during assembly to ensure good coverage.

(4). For Press Fitted Assemblies, apply adhesive thoroughly to both bond surfaces and assemble at high press onrates.

(5). For Shrink Fitted Assemblies the adhesive should be coated onto the pin, the collar should then be heated to create sufficient clearance for free assembly.

(6). Parts should not be disturbed until sufficient handling strength is achieved.

6:For Disassembly

Apply localized heat to the assembly to approximately

250 °C. Disassemble while hot.

7:For Clean up

Cured product can be removed with a combination of soaking in a HENG YING solvent and mechanical abrasion such as a wire brush.

8:Storage

Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.

Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container.HYBOND Corporation cannot assume responsibility for product which

has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

Loctite 620 Equivalent Anaerobic Threadlocker Adhesive

               Loctite 620 Equivalent Anaerobic Threadlocker Adhesive

                                                               from Shirley(hengying@cnhybond.com   0086-18927302778  Skype:hengying11)

1:PRODUCT DESCRIPTION

HYBOND 620 provides the following product characteristics:

Technology: Acrylic

Chemical Type: methacrylate ester

Appearance (uncured): Green  liquidLMS

MComponents:  One component - requires no mixing

Viscosity: high

Cure : Anaerobic

Secondary Cure: Activator

Application :Retaining

Strength: Medium to high

HYBOND 620 is designed for the bonding of cylindrical fitting parts. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. Typical applications include locating pins in radiator assemblies, sleeves into pump housings and bearings in auto transmissions. Particularlysuitable for applications where temperature resistance up to 200°C is required.

2: TYPICAL PROPERTIES OF UNCURED MATERIAL

M LM Specific Gravity @ 25 °C 1.16

Flash Point - See MSDS

Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP):

Spindle 5, speed 20 rpm 5,000 to 12,000LMS

Viscosity, EN 12092 - MV, 25 °C, after 180 s, mPa·s (cP):

Shear rate 129 s-1 1,200 to 2,400S

3:TYPICAL PROPERTIES OF CURED MATERIAL

Physical Properties:

Coefficient of Thermal Expansion, ASTM D 696, K-1 80×10-6

Coefficient of Thermal Conductivity, ASTM C 177,

W/(m·K)

0.10

Specific Heat, kJ/(kg·K) 0.30

Elongation, at break, ASTM D 412, % <1

4:TYPICAL PERFORMANCE OF CURED MATERIAL

Adhesive Properties

After 24 hours @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥17.20LMS

(psi) (2,495)

Cured for 24 hours @ 22 °C, followed by 24 hours @ 177 °C,

tested @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥24.10LMS

(psi) (3,495)

5:For Assembly

(1). For best results, clean all surfaces (external and internal) with a HYBOND cleaning solvent and allow to dry.

(2). If the material is an inactive metal or the cure speed is too slow, spray with Activator  7649™ and allow to dry.

(3). For Slip Fitted Assemblies, apply adhesive around the leading edge of the pin and the inside of the collar and use a rotating motion during assembly to ensure good coverage.

(4). For Press Fitted Assemblies, apply adhesive thoroughly to both bond surfaces and assemble at high press onrates.

(5). For Shrink Fitted Assemblies the adhesive should be coated onto the pin, the collar should then be heated to create sufficient clearance for free assembly.

6:For Disassembly

Apply localized heat to the assembly to approximately

250 °C. Disassemble while hot.

7:For Clean up

Cured product can be removed with a combination of soaking in a HENG YING solvent and mechanical abrasion such as a wire brush.

8:Storage

Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.

Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container.HYBOND Corporation cannot assume responsibility for product which

has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

Loctite 641 Equivalent Cylindrical Bonding Retaining Compound

    Loctite 641 Equivalent Cylindrical Bonding Retaining Compound

                                   from Shirley(hengying@cnhybond.com   0086-18927302778   Skype:hengying11)

Product Description
CNHYBOND 641™ provides the following product

characteristics:
Technology: Acrylic

Chemical Type:methacrylate Ester

Appearance(uncured):yellow liquid

Components:One component - requires no mixing

Viscosity:Medium

Cure:Anaerobic

Secondary Cure:Activator

Application:Retaining

Strength:Medium

CNHYBOND 641™ is designed for the bonding of cylindrical fitting parts. particularly where disassembly is required for service operations. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. Typical applications include retention of bearings onto shafts and into housings.

Typical Properties of Uncured Material 

Specific Gravity @ 25 °C 1.0

Flash Point - See MSDS

Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP):

Spindle 2, speed 20 rpm ,200 to 2,600LMS

Viscosity, EN 12092 - MV, 25 °C, after 180 s, mPa·s (cP):

Shear rate 129 s-1 90-180

3:Typical Properties of Cured Material 

Physical Properties

Coefficient of Thermal Expansion,ASTM D696,K-1 80×10-6

Coefficient of Thermal Conductivity, ASTM C177,W/(m·K)  0.1
Specific Heat, kJ/(kg·K) 0.3

4:Typical Performance of Cured Material 

Adhesive Properties

Adhesive Properties  Cured for 15 minutes @ 22 °C
Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥6.5LMS   (psi) (≥940)

5:For Assembly

(1). For best results, clean all surfaces (external and internal) with a HYBOND  cleaning solvent and allow to dry.

(2). If the material is an inactive metal or the cure speed is too slow, spray with Activator  7649™ and allow to dry.

(3). For Slip Fitted Assemblies, apply adhesive around the leading edge of the pin and the inside of the collar and use a rotating motion during assembly to ensure good coverage.

(4). For Press Fitted Assemblies, apply adhesive thoroughly to both bond surfaces and assemble at high press on rates.

(5). For Shrink Fitted Assemblies the adhesive should be coated onto the pin, the collar should then be heated to create sufficient clearance for free assembly.

(6). Parts should not be disturbed until sufficient handling strength is achieved

6:For Disassembly

Apply localized heat to the assembly to approximately 250 °C. Disassemble while hot.

7:For Clean up

Cured product can be removed with a combination of soaking in a HENG YING solvent and mechanical abrasion such as a wire brush.

8:Storage

Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.

Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container.HYBOND Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

We have new company pages on facebook, google,linkedin, and please follow us, thank you.

https://www.linkedin.com/company/huizhou-heng-ying-adhesive-product-co-ltd?trk=biz-companies-cym

https://www.facebook.com/pages/Heng-Ying-Adhesive-CoLtd/862427133801944

https://plus.google.com/u/0/b/117466620353553764866/117466620353553764866/admin/?tab=XX#117466620353553764866/posts?tab=XX